Rubber compositions containing N-(4-hydroxyphenyl) stearamide

ABSTRACT

The present invention relates to rubber compositions containing N-(4-hydroxyphenyl) stearamide. The presence of N-(4-hydroxyphenyl) stearamide improves the physical properties of the rubber including flex fatigue resistance.

FIELD OF THE INVENTION

The present invention relates to a rubber composition containing N-(4-hydroxyphenyl) stearamide and the processing of rubber compositions containing N-(4-hydroxyphenyl) stearamide.

BACKGROUND OF THE INVENTION

Processing aids are commonly used in both natural and synthetic rubber compositions. Such processing aids are used during the mixing, permitting incorporation of fillers and other ingredients rapidly with lower power consumption. In instances where the filler is silica, well-known sulfur containing organosilicon compounds are used to further assist in compatibilizing the silica in the rubber composition.

SUMMARY OF THE INVENTION

The present invention relates to the use of N-(4-hydroxyphenyl) stearamide in a rubber composition.

DETAILED DESCRIPTION OF THE INVENTION

There is disclosed a method for processing a rubber composition which comprises mixing

(i) 100 parts by weight of at least one elastomer containing olefinic unsaturation selected from the group consisting of natural rubber and conjugated diene homopolymers and copolymers and from copolymers of at least one conjugated diene and aromatic vinyl compound; with

(ii) 0.05 to 10 phr of N-(4-hydroxyphenyl) stearamide.

There is also disclosed a rubber composition comprising an elastomer containing olefinic unsaturation and an N-(4-hydroxyphenyl) stearamide.

The present invention may be used to process rubbers or elastomers containing olefinic unsaturation. The phrase "rubber or elastomer containing olefinic unsaturation" is intended to include both natural rubber and its various raw and reclaim forms as well as various synthetic rubbers. In the description of this invention, the terms "rubber" and "elastomer" may be used interchangeably, unless otherwise prescribed. The terms "rubber composition," "compounded rubber" and "rubber compound" are used interchangeably to refer to rubber which has been blended or mixed with various ingredients and materials and such terms are well known to those having skill in the rubber mixing or rubber compounding art. Representative synthetic polymers are the homopolymerization products of butadiene and its homologues and derivatives, for example, methylbutadiene, dimethylbutadiene and pentadiene as well as copolymers such as those formed from butadiene or its homologues or derivatives with other unsaturated monomers. Among the latter are acetylenes, for example, vinyl acetylene; olefins, for example, isobutylene, which copolymerizes with isoprene to form butyl rubber; vinyl compounds, for example, acrylic acid, acrylonitrile (which polymerize with butadiene to form NBR), methacrylic acid and styrene, the latter compound polymerizing with butadiene to form SBR, as well as vinyl esters and various unsaturated aldehydes, ketones and ethers, e.g., acrolein, methyl isopropenyl ketone and vinylethyl ether. Specific examples of synthetic rubbers include neoprene (polychloroprene), polybutadiene (including cis-1,4-polybutadiene), polyisoprene (including cis-1,4-polyisoprene), butyl rubber, styrene/isoprene/butadiene rubber, copolymers of 1,3-butadiene or isoprene with monomers such as styrene, acrylonitrile and methyl methacrylate, as well as ethylene/propylene terpolymers, also known as ethylene/propylene/diene monomer (EPDM), and, in particular, ethylene/propylene/dicyclopentadiene terpolymers. The preferred rubber or elastomers are polybutadiene and SBR.

In one aspect, the rubber is preferably of at least two of diene-based rubbers. For example, a combination of two or more rubbers is preferred such as cis 1,4-polyisoprene rubber (natural or synthetic, although natural is preferred), 3,4-polyisoprene rubber, styrene/isoprene/butadiene rubber, emulsion and solution polymerization derived styrene/butadiene rubbers, cis 1,4-polybutadiene rubbers and emulsion polymerization prepared butadiene/acrylonitrile copolymers.

In one aspect of this invention, an emulsion polymerization derived styrene/butadiene (E-SBR) might be used having a relatively conventional styrene content of about 20 to about 28 percent bound styrene or, for some applications, an E-SBR having a medium to relatively high bound styrene content; namely, a bound styrene content of about 30 to about 45 percent.

The relatively high styrene content of about 30 to about 45 for the E-SBR can be considered beneficial for a purpose of enhancing traction, or skid resistance, of the tire tread. The presence of the E-SBR itself is considered beneficial for a purpose of enhancing processability of the uncured elastomer composition mixture, especially in comparison to a utilization of a solution polymerization prepared SBR (S-SBR).

By emulsion polymerization prepared E-SBR, it is meant that styrene and 1,3-butadiene are copolymerized as an aqueous emulsion. Such are well known to those skilled in such art. The bound styrene content can vary, for example, from about 5 to about 50 percent. In one aspect, the E-SBR may also contain acrylonitrile to form a terpolymer rubber, as E-SBAR, in amounts, for example, of about 2 to about 30 weight percent bound acrylonitrile in the terpolymer.

Emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubbers containing about 2 to about 40 weight percent bound acrylonitrile in the terpolymer are also contemplated as diene-based rubbers for use in this invention.

The solution polymerization prepared SBR (S-SBR) typically has a bound styrene content in a range of about 5 to about 50, preferably about 9 to about 36, percent. The S-SBR can be conveniently prepared, for example, by organo lithium catalyzation in the presence of an organic hydrocarbon solvent.

A purpose of using S-SBR is for improved tire rolling resistance as a result of lower hysteresis when it is used in a tire tread composition.

The 3,4-polyisoprene rubber (3,4-PI) is considered beneficial for a purpose of enhancing the tire's traction when it is used in a tire tread composition. The 3,4-PI and use thereof is more fully described in U.S. Pat. No. 5,087,668 which is incorporated herein by reference. The Tg refers to the glass transition temperature which can conveniently be determined by a differential scanning calorimeter at a heating rate of 10° C. per minute.

The cis 1,4-polybutadiene rubber (BR) is considered to be beneficial for a purpose of enhancing the tire tread's wear, or treadwear. Such BR can be prepared, for example, by organic solution polymerization of 1,3-butadiene. The BR may be conveniently characterized, for example, by having at least a 90 percent cis 1,4-content.

The cis 1,4-polyisoprene and cis 1,4-polyisoprene natural rubber are well known to those having skill in the rubber art.

The term "phr" as used herein, and according to conventional practice, refers to "parts by weight of a respective material per 100 parts by weight of rubber, or elastomer."

N-(4-hydroxyphenyl) stearamide, also known as N-stearoyl-p-aminophenol is a known antioxidant for polyethylene and polyamides. N-(4-hydroxyphenyl) stearamide is a white powder having a melting point of from 130-134° C.

The N-(4-hydroxyphenyl) stearamide used in the present invention may be added to the rubber by any conventional technique such as on a mill or in a Banbury. The amount of N-(4-hydroxyphenyl) stearamide may vary widely depending on the type of rubber and other compounds present in the rubber composition. Generally, the amount of N-(4-hydroxyphenyl) stearamide is used in a range of from about 0.05 to about 10.0 phr with a range of 0.1 to about 5.0 phr being preferred. The N-(4-hydroxyphenyl) stearamide may be added during the nonproductive stage or productive stage of mixing but is preferably added in the nonproductive stage.

For ease in handling, the N-(4-hydroxyphenyl) stearamide may be used per se or may be deposited on suitable carriers. Examples of carriers which may be used in the present invention include silica, carbon black, alumina, kieselguhr, silica gel and calcium silicate.

In one embodiment, the rubber composition contains a sufficient amount of filler to contribute a reasonably high modulus and high resistance to tear. The filler may be added in amounts ranging from 10 to 250 phr. When the filler is silica, the silica is generally present in an amount ranging from 10 to 80 phr. Preferably, the silica is present in an amount ranging from 15 to 70 phr. When the filler is carbon black, the amount of carbon black will vary from 0 to 80 phr. Preferably, the amount of carbon black will range from 0 to 40 phr.

The commonly employed particulate precipitated silica used in rubber compounding applications can be used as the silica in this invention. These precipitated silicas include, for example, those obtained by the acidification of a soluble silicate; e.g., sodium silicate.

Such silicas might be characterized, for example, by having a BET surface area, as measured using nitrogen gas, preferably in the range of about 40 to about 600, and more usually in a range of about 50 to about 300 square meters per gram. The BET method of measuring surface area is described in the Journal of the American Chemical Society, Volume 60, page 304 (1930).

The silica may also be typically characterized by having a dibutylphthalate (DBP) absorption value in a range of about 100 to about 400, and more usually about 150 to about 300.

The silica might be expected to have an average ultimate particle size, for example, in the range of 0.01 to 0.05 micron as determined by the electron microscope, although the silica particles may be even smaller, or possibly larger, in size.

Various commercially available silicas may be considered for use in this invention such as, only for example herein, and without limitation, silicas commercially available from PPG Industries under the Hi-Sil trademark with designations 210, 243, etc; silicas available from Rhone-Poulenc, with, for example, designations of Z1165MP and Z165GR and silicas available from Degussa AG with, for example, designations VN2 and VN3, etc.

The processing of the sulfur vulcanizable rubber may be conducted in the presence of a sulfur containing organosilicon compound. Examples of suitable sulfur containing organosilicon compounds are of the formula:

    Z--Alk--S.sub.n --Alk--Z                                   (I)

in which Z is selected from the group consisting of ##STR1## where R¹ is an alkyl group of 1 to 4 carbon atoms, cyclohexyl or phenyl;

R² is alkoxy of 1 to 8 carbon atoms, or cycloalkoxy of 5 to 8 carbon atoms;

Alk is a divalent hydrocarbon of 1 to 18 carbon atoms and n is an integer of 2 to 8.

Specific examples of sulfur containing organosilicon compounds which may be used in accordance with the present invention include: 3,3'-bis(trimethoxysilylpropyl) disulfide, 3,3'-bis(triethoxysilylpropyl) tetrasulfide, 3,3'-bis(triethoxysilylpropyl) octasulfide, 3,3'-bis(trimethoxysilylpropyl) tetrasulfide, 2,2'-bis(triethoxysilylethyl) tetrasulfide, 3,3'-bis(trimethoxysilylpropyl) trisulfide, 3,3'-bis(triethoxysilylpropyl) trisulfide, 3,3'-bis(tributoxysilylpropyl) disulfide, 3,3'-bis(trimethoxysilylpropyl) hexasulfide, 3,3'-bis(trimethoxysilylpropyl) octasulfide, 3,3'-bis(trioctoxysilylpropyl) tetrasulfide, 3,3'-bis(trihexoxysilylpropyl) disulfide, 3,3'-bis(tri-2"-ethylhexoxysilylpropyl) trisulfide, 3,3'-bis(triisooctoxysilylpropyl) tetrasulfide, 3,3'-bis(tri-t-butoxysilylpropyl) disulfide, 2,2'-bis(methoxy diethoxy silyl ethyl) tetrasulfide, 2,2'-bis(tripropoxysilylethyl) pentasulfide, 3,3'-bis(tricyclohexoxysilylpropyl) tetrasulfide, 3,3'-bis(tricyclopentoxysilylpropyl) trisulfide, 2,2'-bis(tri-2"-methylcyclohexoxysilylethyl) tetrasulfide, bis(trimethoxysilylmethyl) tetrasulfide, 3-methoxy ethoxy propoxysilyl 3'-diethoxybutoxysilylpropyltetrasulfide, 2,2'-bis(dimethyl methoxysilylethyl) disulfide, 2,2'-bis(dimethyl sec.butoxysilylethyl) trisulfide, 3,3'-bis(methyl butylethoxysilylpropyl) tetrasulfide, 3,3'-bis(di t-butylmethoxysilylpropyl) tetrasulfide, 2,2'-bis(phenyl methyl methoxysilylethyl) trisulfide, 3,3'-bis(diphenyl isopropoxysilylpropyl) tetrasulfide, 3,3'-bis(diphenyl cyclohexoxysilylpropyl) disulfide, 3,3'-bis(dimethyl ethylmercaptosilylpropyl) tetrasulfide, 2,2'-bis(methyl dimethoxysilylethyl) trisulfide, 2,2'-bis(methyl ethoxypropoxysilylethyl) tetrasulfide, 3,3'-bis(diethyl methoxysilylpropyl) tetrasulfide, 3,3'-bis(ethyl di-sec. butoxysilylpropyl) disulfide, 3,3'-bis(propyl diethoxysilylpropyl) disulfide, 3,3'-bis(butyl dimethoxysilylpropyl) trisulfide, 3,3'-bis(phenyl dimethoxysilylpropyl) tetrasulfide, 3-phenyl ethoxybutoxysilyl 3'-trimethoxysilylpropyl tetrasulfide, 4,4'-bis(trimethoxysilylbutyl) tetrasulfide, 6,6'-bis(triethoxysilylhexyl) tetrasulfide, 12,12'-bis(triisopropoxysilyl dodecyl) disulfide, 18,18'-bis(trimethoxysilyloctadecyl) tetrasulfide, 18,18'-bis(tripropoxysilyloctadecenyl) tetrasulfide, 4,4'-bis(trimethoxysilyl-buten-2-yl) tetrasulfide, 4,4'-bis(trimethoxysilylcyclohexylene) tetrasulfide, 5,5'-bis(dimethoxymethylsilylpentyl) trisulfide, 3,3'-bis(trimethoxysilyl-2-methylpropyl) tetrasulfide, 3,3'-bis(dimethoxyphenylsilyl-2-methylpropyl) disulfide.

The preferred sulfur containing organosilicon compounds are the 3,3'-bis(trimethoxy or triethoxy silylpropyl) sulfides. The most preferred compound is 3,3'-bis(triethoxysilylpropyl) tetrasulfide. Therefore, as to Formula I, preferably Z is ##STR2## where R² is an alkoxy of 2 to 4 carbon atoms, with 2 carbon atoms being particularly preferred; Alk is a divalent hydrocarbon of 2 to 4 carbon atoms with 3 carbon atoms being particularly preferred; and n is an integer of from 3 to 5 with 4 being particularly preferred.

The amount of the sulfur containing organosilicon compound of Formula I in a rubber composition will vary depending on the level of silica that is used. Generally speaking, the amount of the compound of formula II, if used, will range from 0.01 to 1.0 parts by weight per part by weight of the silica. Preferably, the amount will range from 0.05 to 0.4 parts by weight per part by weight of the silica.

The rubber compositions of the present invention may contain a methylene donor and a methylene acceptor. The term "methylene donor" is intended to mean a compound capable of reacting with a methylene acceptor (such as resorcinol or its equivalent containing a present hydroxyl group) and generate the resin in-situ. N-(4-hydroxyphenyl) stearamide may function as a methylene acceptor in place of resorcinol when methylene donors are used. Examples of methylene donors which are suitable for use in the present invention include hexamethylenetetramine, hexaethoxymethylmelamine, hexamethoxymethylmelamine, lauryloxymethylpyridinium chloride, ethoxymethylpyridinium chloride, trioxan hexamethoxymethylmelamine, the hydroxy groups of which may be esterified or partly esterified, and polymers of formaldehyde such as paraformaldehyde. In addition, the methylene donors may be N-substituted oxymethylmelamines, of the general formula: ##STR3## wherein X is an alkyl having from 1 to 8 carbon atoms, R³, R⁴, R⁵, R⁶ and R⁷ are individually selected from the group consisting of hydrogen, an alkyl having from 1 to 8 carbon atoms and the group --CH₂ OX. Specific methylene donors include hexakis(methoxymethyl)melamine, N,N',N"-trimethyl/N,N',N"-trimethylolmelamine, hexamethylolmelamine, N,N',N"-dimethylolmelamine, N-methylolmelamine, N,N'-dimethylolmelamine, N,N',N"-tris(methoxymethyl)melamine and N,N',N"-tributyl-N,N',N"-trimethylol-melamine. The N-methylol derivatives of melamine are prepared by known methods.

The amount of methylene donor and methylene acceptor that is present in the rubber stock may vary. Typically, the amount of methylene donor and methylene acceptor that are present will range from about 0.1 phr to 10.0 phr. Preferably, the amount of methylene donor and methylene acceptor ranges from about 2.0 phr to 5.0 phr for each.

The weight ratio of methylene donor to the methylene acceptor may vary. Generally speaking, the weight ratio will range from about 1:10 to about 10:1. Preferably, the weight ratio ranges from about 1:3 to 3:1.

It is readily understood by those having skill in the art that the rubber composition would be compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable constituent rubbers with various commonly used additive materials such as, for example, sulfur donors, curing aids, such as activators and retarders and processing additives, such as oils, resins including tackifying resins and plasticizers, fillers, pigments, fatty acid, zinc oxide, waxes, antioxidants and antiozonants and peptizing agents. As known to those skilled in the art, depending on the intended use of the sulfur vulcanizable and sulfur vulcanized material (rubbers), the additives mentioned above are selected and commonly used in conventional amounts. Typical amounts of reinforcing type carbon blacks(s), for this invention, if used, are herein set forth. Representative examples of sulfur donors include elemental sulfur (free sulfur), an amine disulfide, polymeric polysulfide and sulfur olefin adducts. Preferably, the sulfur vulcanizing agent is elemental sulfur. The sulfur vulcanizing agent may be used in an amount ranging from 0.5 to 8 phr, with a range of from 1.5 to 6 phr being preferred. Typical amounts of tackifier resins, if used, comprise about 0.5 to about 10 phr, usually about 1 to about 5 phr. Typical amounts of processing oils comprise about 1 to about 50 phr. Such processing aids can include, for example, aromatic, naphthenic and/or paraffinic processing oils. Typical amounts of antioxidants comprise about 1 to about 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in the Vanderbilt Rubber Handbook (1978), pages 344-346. Typical amounts of antiozonants comprise about 1 to 5 phr. Typical amounts of fatty acids, if used, which can include stearic acid comprise about 0.5 to about 3 phr. Typical amounts of zinc oxide comprise about 2 to about 5 phr. Typical amounts of microcrystalline and paraffinic waxes comprise about 1 to about 10 phr. Often microcrystalline waxes are used. Typical amounts of peptizers comprise about 0.1 to about 1 phr. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide.

In one aspect of the present invention, the sulfur vulcanizable rubber composition is then sulfur-cured or vulcanized.

Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used; i.e., primary accelerator. The primary accelerator(s) may be used in total amounts ranging from about 0.5 to about 4, preferably about 0.8 to about 1.5, phr. In another embodiment, combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in smaller amounts, such as from about 0.05 to about 3 phr, in order to activate and to improve the properties of the vulcanizate. Combinations of these accelerators might be expected to produce a synergistic effect on the final properties and are somewhat better than those produced by use of either accelerator alone. In addition, delayed action accelerators may be used which are not affected by normal processing temperatures but produce a satisfactory cure at ordinary vulcanization temperatures. Vulcanization retarders might also be used. Suitable types of accelerators that may be used in the present invention are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. Preferably, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound.

The mixing of the rubber composition can be accomplished by methods known to those having skill in the rubber mixing art. For example, the ingredients are typically mixed in at least two stages; namely, at least one non-productive stage followed by a productive mix stage. The final curatives including sulfur vulcanizing agents are typically mixed in the final stage which is conventionally called the "productive" mix stage in which the mixing typically occurs at a temperature, or ultimate temperature, lower than the mix temperature(s) than the preceding non-productive mix stage(s). The rubber and N-(4-hydroxyphenyl) stearamide are mixed in one or more non-productive mix stages. The terms "non-productive" and "productive" mix stages are well known to those having skill in the rubber mixing art. The rubber composition containing the N-(4-hydroxyphenyl) stearamide, rubber, silica and sulfur-containing organosilicon compound, if used, may be subjected to a thermomechanical mixing step. The thermomechanical mixing step generally comprises a mechanical working in a mixer or extruder for a period of time suitable in order to produce a rubber temperature between 140° C. and 190° C. The appropriate duration of the thermomechanical working varies as a function of the operating conditions and the volume and nature of the components. For example, the thermomechanical working may be from 4 to 20 minutes.

Vulcanization of the rubber composition of the present invention is generally carried out at conventional temperatures ranging from about 100° C. to 200° C. Preferably, the vulcanization is conducted at temperatures ranging from about 110° C. to 180° C. Any of the usual vulcanization processes may be used such as heating in a press or mold, heating with superheated steam or hot air or in a salt bath.

Upon vulcanization of the sulfur vulcanized composition, the rubber composition of this invention can be used for various purposes. For example, the sulfur vulcanized rubber composition may be in the form of a tire, belt or hose. In case of a tire, it can be used for various tire components. Such tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art. Preferably, the rubber composition is used in the tread of a tire. As can be appreciated, the tire may be a passenger tire, aircraft tire, truck tire and the like. Preferably, the tire is a passenger tire. The tire may also be a radial or bias, with a radial tire being preferred.

The invention may be better understood by reference to the following examples in which the parts and percentages are by weight unless otherwise indicated.

The following examples are presented in order to illustrate but not limit the present invention.

Cure properties were determined using a Monsanto oscillating disc rheometer which was operated at a temperature of 150° C. and at a frequency of 11 hertz. A description of oscillating disc rheometers can be found in the Vanderbilt Rubber Handbook edited by Robert O. Ohm (Norwalk, Conn., R. T. Vanderbilt Company, Inc., 1990), pages 554-557. The use of this cure meter and standardized values read from the curve are specified in ASTM D-2084. A typical cure curve obtained on an oscillating disc rheometer is shown on page 555 of the 1990 edition of the Vanderbilt Rubber Handbook.

In such an oscillating disc rheometer, compounded rubber samples are subjected to an oscillating shearing action of constant amplitude. The torque of the oscillating disc embedded in the stock that is being tested that is required to oscillate the rotor at the vulcanization temperature is measured. The values obtained using this cure test are very significant since changes in the rubber or the compounding recipe are very readily detected. It is obvious that it is normally advantageous to have a fast cure rate.

The invention may be better understood by reference to the following examples in which the parts and percentages are by weight unless otherwise indicated.

EXAMPLE 1 Preparation of N-(4-Hydroxyphenyl) Stearamide

A 3-liter flask was charged with 218 grams (2 moles) of 4-aminophenol, 538 grams (1.9 moles) of stearic acid, 20 grams of p-toluenesulfonic acid, 300 ml of xylene and swept with nitrogen. The flask was fitted with a Dean-Stark trap for water removal and the contents heated with stirring to 220° C. with water and xylene removal for 2 hours. Twenty-eight milliliters of water were removed. The contents of the flask were cooled to 110° C. and poured into a polyethylene container, which was stripped of volatiles at 125-130° C. at 29 inches of Hg vacuum to give 737 grams of a waxy solid with an infrared spectroscopic spectra showing phenolic and amide functional groups.

EXAMPLE 2

In this example, various levels of N-(4-hydroxyphenyl) stearamide were evaluated in a rubber compound.

Rubber compositions containing the materials set out in Tables 1 and 2 were prepared in a BR Banbury™ mixer using two separate stages of addition (mixing); namely, one non-productive mix stage and one productive mix stage. The non-productive stage was mixed for up to 4 minutes or to a rubber temperature of 160° C. whichever occurred first. The mixing time for the productive stage was to a rubber temperature of 110° C. for 2 minutes.

The rubber compositions are identified herein as Samples 1-4. Sample 1 is considered herein as being a control without the use of any N-(4-hydroxyphenyl) stearamide added to the rubber composition. Other than the level of rosin acid and N-(4-hydroxyphenyl) stearamide, each rubber composition was the same.

The samples were cured at about 150° C. for about 36 minutes.

Table 2 illustrates the behavior and physical properties of the cured samples 1-4.

It is clearly evident from the results that the use of N-(4-hydroxyphenyl) stearamide in a rubber compound provides lower minimum Rheometer torque which would indicate less work input required during Banbury mixing and an improved processing compound. The N-(4-hydroxyphenyl) stearamide also provide improved flex properties as measured by the Cut Growth test. The reduced DIN abrasion suggests that improved treadwear would be realized in a tire.

                  TABLE 1     ______________________________________     Samples      1        2        3      4     ______________________________________     Non-Productive     Emulsion SBR.sup.1                  100      100      100    100     Carbon Black.sup.2                  65       65       65     65     Processing Aids.sup.3                  25.5     25.5     25.5   25.5     Fatty Acids  2        2        2      2     Antiozonant.sup.4                  3.5      3.5      3.5    3.5     Rosin Acid   5        0        0      0     N-(4-Hydroxyphenyl)                  0        5        10     17     stearamide     Productive     Antioxidant.sup.5                  1.15     1.15     1.15   1.15     Zinc Oxide   3        3        3      3     Sulfur       1.5      1.5      1.5    1.5     Accelerators.sup.6                  2.7      2.7      2.7    2.7     ______________________________________      .sup.1 Emulsion SBR containing 23.5% styrene and is commercially availabl      from The Goodyear Tire & Rubber Company as PLF 1502.      .sup.2 N299 carbon black      .sup.3 Aromatic oil, waxes, tackifier      .sup.4 Nphenyl-N(1,3-dimethylbutyl)-p-phenylenediamine      .sup.5 Mixed diarylp-phenylenediamine      .sup.6 Sulfenamide types

                  TABLE 2     ______________________________________     Sample       1        2        3      4     ______________________________________     Rosin Acid (phr)                  5        0        0      0     N-(4-hydroxyphenyl)                  0        5        10     17     stearamide (Phr)     Rheometer 150° C.     T90          10.5     8.5      9.2    10.5     Min Torque   6.3      5.1      4.8    4.5     Max Torque   31.2     29.9     21.9   18.0     Delta Torque 24.9     24.8     17.1   13.5     Final Torque 31.0     29.8     21.8   17.3     Stress Strain 36' @ 150° C.     100% Modulus (MPa)                  1.88     1.97     1.95   1.97     300% Modulus (MPa)                  7.33     8.56     7.16   5.94     Tens Strength (MPa)                  15.3     15.8     14.2   12.3     Elong @ Break (%)                  613      547      589    626     Hardness     RT           66       67       70     74     100 C        49       52       51     49     Rebound     RT           31       31       30     30     100° C.                  42       44       41     39     Compression Set.sup.1     % Set        15.6     13.6     17.6   28.3     Hot Din Abrasion (100° C.)     Rel Vol Loss 152      131      127    135     Cut Growth.sup.2     (Cycles to failure                  4.76     15.5     28.1   28.0     × 10.sup.5)     ______________________________________      .sup.1 ASTM D395      .sup.2 Cut growth test described in Rubber Chem & Tech, Sept-Oct 1990,      Volume 63, No. 4, pages 567-581.

While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in this art that various changes and modifications may be made therein without departing from the spirit or scope of the invention. 

What is claimed is:
 1. A method of processing a rubber composition which comprises mixing(i) 100 parts by weight of at least one elastomer containing olefinic unsaturation selected the group consisting of natural rubber, conjugated diene homopolymers and copolymers and from copolymers of at least one conjugated diene and aromatic vinyl compound; with (ii) 0.05 to 10 phr of N-(4-hydroxyphenyl) stearamide.
 2. The method of claim 1 wherein said N-(4-hydroxyphenyl) stearamide is added in an amount ranging from 0.10 to 5.0 phr.
 3. The method of claim 1 wherein a methylene donor is present in said rubber composition.
 4. The method of claim 3 wherein said methylene donor is selected from the group consisting of hexamethylenetetramine, hexaethoxymethylmelamine, hexamethoxymethylmelamine, lauryloxymethylpyridinium chloride, ethoxymethylpyridinium chloride, trioxan hexamethoxymethylmelamine, the hydroxy groups of which may be esterified or partly esterified, and polymers of formaldehyde.
 5. The method of claim 3 wherein said methylene donor is selected from the group of N-substituted oxymethylmelamines of the general formula ##STR4## wherein X is an alkyl having from 1 to 8 carbon atoms, R³, R⁴, R⁵, R⁶ and R⁷ are individually selected from the group consisting of hydrogen, an alkyl having from 1 to 8 carbon atoms and the group --CH₂ OX.
 6. The method of claim 5 wherein said methylene donor is selected from the group consisting of hexakis-(methoxymethyl)melamine, N,N',N"-trimethyl/N,N',N"-trimethylolmelamine, hexamethylolmelamine, N,N',N"-dimethylolmelamine, N-methylolmelamine, N,N'-dimethylolmelamine, N,N',N"-tris(methoxymethyl)melamine and N,N',N"-tributyl-N,N',N"-trimethylol-melamine.
 7. The method of claim 3 wherein the amount of methylene donor ranges from 0.1 to 10 phr.
 8. The method of claim 1 wherein said elastomer containing olefinic unsaturation is selected from the group consisting of natural rubber, neoprene, polyisoprene, butyl rubber, polybutadiene, styrene-butadiene copolymer, styrene/isoprene/butadiene rubber, methyl methacrylate-butadiene copolymer, isoprene-styrene copolymer, methyl methacrylate-isoprene copolymer, acrylonitrile-isoprene copolymer, acrylonitrile-butadiene copolymer, EPDM and mixtures thereof.
 9. A rubber composition comprising an elastomer containing olefinic unsaturation and 0.05 to 10 phr of N-(4-hydroxyphenyl) stearamide.
 10. The composition of claim 6 wherein said N-(4-hydroxyphenyl) stearamide is present in an amount ranging from 0.10 to 5.0 phr.
 11. The composition of claim 9 wherein a methylene donor is present in said rubber composition.
 12. The composition of claim 11 wherein said methylene donor is selected from the group consisting of hexamethylenetetramine, hexaethoxymethylmelamine, hexamethoxymethylmelamine, lauryloxymethylpyridinium chloride, ethoxymethylpyridinium chloride, trioxan hexamethoxymethylmelamine, the hydroxy groups of which may be esterified or partly esterified, and polymers of formaldehyde.
 13. The composition of claim 11 wherein said methylene donor is selected from the group of N-substituted oxymethylmelamines of the general formula: ##STR5## wherein X is an alkyl having from 1 to 8 carbon atoms, R³, R⁴, R⁵, R⁶ and R⁷ are individually selected from the group consisting of hydrogen, an alkyl having from 1 to 8 carbon atoms and the group --CH₂ OX.
 14. The composition of claim 13 wherein said methylene donor is selected from the group consisting of hexakis-(methoxymethyl)melamine, N,N',N"-trimethyl/N,N',N"-trimethylolmelamine, hexamethylolmelamine, N,N',N"-dimethylolmelamine, N-methylolmelamine, N,N'-dimethylolmelamine, N,N',N"-tris(methoxymethyl)melamine and N,N',N"-tributyl-N,N',N"-trimethylol-melamine.
 15. The composition of claim 11 wherein the amount of methylene donor ranges from 0.1 to 10.0 phr.
 16. The composition of claim 9 wherein said elastomer containing olefinic unsaturation is selected from the group consisting of natural rubber, neoprene, polyisoprene, butyl rubber, polybutadiene, styrene-butadiene copolymer, styrene/isoprene/butadiene rubber, methyl methacrylate-butadiene copolymer, isoprene-styrene copolymer, methyl methacrylate-isoprene copolymer, acrylonitrile-isoprene copolymer, acrylonitrile-butadiene copolymer, EPDM and mixtures thereof.
 17. A sulfur vulcanized rubber composition which is prepared by heating the composition of claim 9 to a temperature ranging from 100° C. to 200° C. in the presence of a sulfur vulcanizing agent.
 18. The sulfur vulcanized rubber composition of claim 17 in the form of a tire, belt or hose.
 19. A tire having a tread comprised of the composition of claim
 18. 